Generation of mechanically mixed layer during wear in hybrid aluminum MMC under as-cast and age hardened conditions

In the present investigations, dry sliding wear test is conducted using a pin on disc tribometer at room temperature for both the as-cast and age hardening conditions. Al7075 has chosen as the matrix material. The reinforcement used are particles of silicon carbide and alumina with 5 wt%, 10 wt%, and 15 wt%. Hybrid aluminum metal matrix composites are produced utilizing stir casting route for enhancing the wear behavior. In the aluminum matrix, micro-structural characterization reveals the homogeneous mixing of reinforcements. From the investigation, it is observed that composites containing 10% by weight of silicon carbide and aluminum oxide reinforcements with ageing exhibited superior tribological properties. From the micro-structural study, it has been observed that the generation of the mechanically mixed layer in the hybrid aluminum metal matrix composites will lead to a reduction in wear rate.