期刊
JOURNAL OF THE ELECTROCHEMICAL SOCIETY
卷 166, 期 11, 页码 C3488-C3492出版社
ELECTROCHEMICAL SOC INC
DOI: 10.1149/2.0561911jes
关键词
-
资金
- NSF MRI grant [DMR-1429674]
- Southern California Chapter of the Association for Iron & Steel Technology
- California Steel Industries Inc.
- Kellogg Honors College
- NACE Foundation
- Western Area of NACE International
- Western States Corrosion Seminar
- LA section of NACE International
The present work investigates the hot corrosion behavior of Al0.1CoCrFeNi high entropy alloy (HEA) and Ni-base Alloy 718. Electrochemical tests were conducted to characterize the corrosion behavior of Al0.1CoCrFeNi HEA and Alloy 718 in a molten Na2SO4-NaCl eutectic mixture at 750 +/- 5 degrees C in the presence of a platinum catalyzed SO2/air mixture. The morphology of the surface of Al0.1CoCrFeNi HEA and Alloy 718 was investigated using scanning electron microscopy (SEM) as well as energy dispersive spectroscopy (EDS). The results indicate that the polarization resistance of the HEA was higher and the corrosion rate lower in comparison with Alloy 718. SEM and EDS analyses reveal the formation of a dual oxide layer on the HEA that provides a better corrosion barrier compared to the single chromia scale observed on Alloy 718. (C) The Author(s) 2019. Published by ECS.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据