HIGH PERFORMANCE POLYMERS
卷 31, 期 7, 页码 831-842出版社
SAGE PUBLICATIONS LTD
DOI: 10.1177/0954008318802939
关键词
Hyperthermal atomic oxygen; transparent polyimide; polyhedral oligomeric silsesquioxane; erosion; low Earth orbit
资金
- National Natural Science Foundation of China [61804054]
- Fundamental Research Funds for the Central Universities [222201714017]
- Shanghai Sailing Program [17YF1403300]
- Natural Science Foundation of Shanghai [18ZR1410400]
A clear poly(amic acid) was reinforced by a trisilanolphenyl polyhedral oligomeric silsesquioxane (POSS) by direct dissolution, and transparent silicon-reinforced polyimide (Si-RPI) films with different POSS loadings were obtained after curing, showing high transmittance of >90% within 380-800 nm. The Si-RPI films were exposed to a ground hyperthermal atomic oxygen (AO) beam. The erosion depths and derived erosion yields of the materials decreased with POSS loadings. At a 20 wt% POSS loading, the Si-RPI showed an erosion yield of 0.13 x 10(-24) cm(3) atom(-1) at a fluence of 2.79 x 10(20) O atoms cm(-2). Surface morphology and element composition characterization on Si-RPI indicated that SiOx-based passivating layers were formed on surfaces upon the hyperthermal AO attack. This study suggests a facile way of reinforcing Si into transparent polyimide for a promising candidate of spacecraft coating material operating in low Earth orbit.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据