Porous WS2 scaffold; Freeze casting; Gelatin concentration; Cooling temperature; Compressive strength
资金
- National Nature Science Foundation of China [51674304, 51604305]
- China Postdoctoral Science Foundation [2016M592445]
- Postdoctoral Science Foundation of Central South University
Porous WS2 scaffolds with aligned lamellar pore were fabricated by freeze casting, and the pore morphology and size can be well controlled by adjusting the processing parameters during freeze casting process. The results indicated that the porosity and the compressive strength of porous WS2 were greatly affected by the concentration of gelatin. As the gelatin addition increased from 1 to 5 wt%, the porosity of porous WS2 scaffolds with initial solid content of 3 vol% decreased from 95.12 to 90.23%, and their compressive strength increased from 0.22 to 1.16 MPa. Moreover, the lamellar spacing and wall thickness could be tailored from 90 to 320 and 5 to 30 mu m respectively by changing the cooling temperature. And the compressive strength of scaffolds has a slight increase with the decreases of cooling temperature. The porous WS2 scaffold with fine aligned lamellar structure and proper compressive strength are expected to be used for scaffold materials.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据