JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS
卷 111, 期 -, 页码 391-402出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.jpcs.2017.08.037
关键词
Zinc hydroxystannate; Microcapsule; Flame retardancy; Smoke suppression; Poly(vinyl chloride)
资金
- Zhejiang Sci-Tech University [2011R50003]
- Zhejiang Provincial Key Lab. Of Industrial Textile Materials & Manufacturing Tech [111121A4E12326, 11110531271546]
The core-double-shell microcapsules flame retardant has been regarded as a promising additive for improving the fire safety of PVC. In this article, melamine formaldehyde resin (MF)/silicon dioxide (SiO2)/zinc hydroxystannate (ZHS) microcapsule was prepared. The effect of synthetic parameters (such as pH, agitation speed, reaction time and reaction temperature) on the morphologies and sizes of the SiO2/ZHS microcapsules were investigated in details. MF/SiO2/ZHS microcapsule was introduced into PVC to prepare biofunctional composites with excellent fire resistance and smoke suppression. The flammability of PVC composites was characterized by limiting oxygen index (LOI), smoke density (SDR), cone calorimeter test. The results showed that the sample containing 16.4% MF/SiO2/ZHS microcapsule (the mass ratio of MF:SiO2:ZHS = 2.5:2:8) achieved the maximal LOI value of 35.6%, minimal SDR value of 21.2%, and significantly decreased the peak heat release rate from 179.7 kW/m(2) of neat PVC to 108.3 kW/m(2). The thermal behaviors of PVC composites and the morphologies of residues were characterized.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据