Corrosion Inhibition of AZ31 Mg Alloy by Aqueous Selenite (SeO32-)

期刊

JOURNAL OF THE ELECTROCHEMICAL SOCIETY
卷 166, 期 14, 页码 C520-C529

出版社

ELECTROCHEMICAL SOC INC
DOI: 10.1149/2.0911914jes

关键词

-

资金

  1. Army Research Laboratory [W911NF-14-2-0004]
  2. National Science Foundation [0639163]
  3. Direct For Mathematical & Physical Scien
  4. Division Of Chemistry [0639163] Funding Source: National Science Foundation

向作者/读者索取更多资源

An investigation was undertaken to study aqueous selenite as a possible corrosion inhibitor for magnesium alloys. Exposure experiments, anodic and cathodic polarization studies, electrochemical impedance spectroscopy (EIS) studies, morphological analysis, X-ray photoelectron spectroscopy (XPS) and Raman surface analysis were performed on alloy AZ31 during and after exposure in different concentrations of sodium selenite (0.5 mM to 50.0 mM) dissolved in 0.1 M NaCl. Formation of a Se-0 film consisting of both amorphous and crystalline Se-0 was observed after exposure to solutions independent of the selenite concentration. In the case of the highest concentration, precipitation of MgSeO3 was observed on the surface of the Mg alloy samples. Both anodic and cathodic inhibition was observed across the range of concentrations examined. Cathodic inhibition was observed independent of selenite concentration and appeared to arise from the presence of a surface film formed on both the matrix and on Al-Mn particles that inhibited water reduction. Anodic inhibition in electrochemical measurements was evident at lower selenite concentrations. Characterization of the film morphology suggested that film structure was detrimentally affected as concentration of the inhibitor increased. (C) The Author(s) 2019. Published by ECS.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据