Investigation of diffusional interaction between P91 grade ferritic steel and Fe-15 wt.% B alloy and study of kinetics of boride formation at high temperature

In the present study, the feasibility of employing the indigenously developed ferroboron alloy (Fe15 wt.% B) as an alternate neutron shield material in combination with 9Cr-based ferritic steel (P91) clad in future Indian fast breeder reactors (FBR), has been investigated from a metallurgical perspective. Towards this goal, a series of diffusion couple experiments have been conducted at three different temperatures namely, 600, 700 and 800 degrees C for time durations up to 5000 h. The thickness of interaction layer has been monitored using standard metallographic procedures. The experiments revealed that ferroboron/P91 combination exhibited a tendency to form complex intermetallic borides at the interface. The structural and microstructural characterization of the interface confirmed that the reaction layer consists predominantly of borides of Fe and Cr of type FeB, Fe2B, (Fe, Cr) 2B and (Fe, Cr) B. The measured variation of interaction layer thickness as a function of time and temperature have been modelled in terms of diffusion mediated interaction. The growth kinetics of borided layer has followed the parabolic law at each temperature, and the apparent activation energy for boride layer formation is found to be of the order of 115 kJ mol(-1). This indicates that the kinetics of boriding could be governed by diffusion of B into the P91 matrix. Based on the findings of present study, an extrapolative estimate of the clad attack thickness at 550 degrees C for 60 years of operating time has been made and it turns out to be 210 +/- 15 mm, which is less than the clad thickness of FBR shielding subassembly (4 mm) [1]. Thus, this study confirms that at testing temperatures from 550 to 600 degrees C, the ferroboron/P91 steel combination can be safely employed for shielding subassembly applications in fast reactors. (C) 2017 Elsevier B.V. All rights reserved.