期刊
MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS
卷 22, 期 5, 页码 -出版社
UNIV FED SAO CARLOS, DEPT ENGENHARIA MATERIALS
DOI: 10.1590/1980-5373-MR-2019-0316
关键词
Pack process; boron-nitro-carburizing; boron nitride
资金
- Coordenacao de Aperfeicoamento de Pessoal de Nivel Superior - Brasil (CAPES) [001]
The aim of this study is to obtain and characterize surface layers on low carbon steel with the pack boron-nitro-carburizing process. Different mixtures of commercial powders (Turbonit (R) and Ekabor (R)) were used to investigate the case properties, microstructure and phases formation on AISI 1020 steel. A series of experiments were conducted in solid medium with powders blend, with weight proportions of 0/100;25/75;50/50;75/25;100/0 at temperatures of 1000 and 1100 degrees C for 2 and 10 hours. Roughness measurement of all treated specimens was assessed to compare with pre-treatment condition. Hardness profile and comparative analysis of phase structure, morphology and composition was carried out to treatment conditions. Optical microscopy shows differences on layers surface, depth and microstructure case - diffusion zone. Results found indicated that for the same treatment time and temperature, hardness was changed, but the diffusion case depth was kept similar. DRX and XPS indicated the formation of boron nitride after certain treatments.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据