JOURNAL OF MATERIOMICS
卷 5, 期 4, 页码 641-648出版社
ELSEVIER
DOI: 10.1016/j.jmat.2019.06.003
关键词
Barium strontium titanate; Glass modification; Energy storage; Ceramic capacitor
资金
- National Natural Science Foundation of China [51767010]
- Science & Technology Key Research Project of Jiangxi Provincial Education Department [GJJ170760]
A glass with composition of B2O3-Bi2O3-SiO2-CaO-BaO-Al2O3-ZrO2 (BBSZ) modified BaxSr1-xTiO3 (BST, x = 0.3 and 0.4) ceramics were prepared by a conventional solid state reaction method abided by a formula of BST + y%BBSZ (y = 0, 2, 4, 7, and 10, in mass). The effect of BBSZ glass content on the structure, dielectric properties and energy storage characteristics of the ceramics was investigated. The dielectric constant reduced but the endurable electrical strength enhanced due to the BBSZ glass addition in BST ceramics. In particular, the dielectric loss of the ceramics at elevated temperature (e.g. 200 degrees C) can be strongly suppressed from tan delta>20% to tan delta<3% after BBSZ glass modification. For Ba0.3Sr0.7TiO3+2% BBSZ ceramics, an optimized energy storage density (gamma = 0.63 J/cm(3)) and efficiency (eta = 91.6%) under an applied electric field of 160 kV/cm was obtained at room temperature. Meanwhile, the temperature dependent polarization-electric field (P-E) hysteresis loops were measured to evaluate the energy storage characteristics of the ceramics potential for high voltage capacitor application at elevated temperatures. (C) 2019 The Chinese Ceramic Society. Production and hosting by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据