期刊
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
卷 33, 期 11, 页码 1323-1328出版社
JOURNAL MATER SCI TECHNOL
DOI: 10.1016/j.jmst.2017.03.010
关键词
Nanostructured copper matrix composites; Minor alloying; Annealing; Grain growth; Particle coarsening
资金
- China Scholarship Council (CSC)
- National Natural Science Foundation of China [51271115]
- Ministry of Science and Technology, China [2012CB619600]
- SJTU-UNSW Strategic Collaboration
Both the coarsening of Al2O3 nanoparticles and the growth of Cu nanograins of mechanically milled nanostructured Cu-5vol.% Al2O3 composites with, and without, trace amounts of Ti during annealing at 973 K for 1 h were investigated. It was found that doping with a small amount of Ti (e.g. 0.2 wt%) in a nanostructured Cu-5vol.% Al2O3 composite effectively suppressed the coarsening of Al2O3 nanoparticles during exposure at this temperature. Further, the Ti addition also prevented the concomitant abnormal growth of the copper grains normally caused by the coarsening of the Al2O3 nanoparticles. Energy dispersive X-ray spectroscopy analysis of the Al2O3 nanoparticles in the annealed Cu-5vol.% Al2O3-0.2wt% Ti sample suggested that the Ti atoms either diffused into the Al2O3 nanoparticles or segregated to the Cu/Al2O3 interfaces to form Ti-doped Al2O3 nanoparticles, which was more stable than Ti-free Al2O3 nanoparticles during annealing at high homologous temperatures. (C) 2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据