Effect of Normalizing Temperature on Fracture Characteristic of Tensile and Impact Tested Creep Strength-Enhanced Ferritic P92 Steel

The high-temperature Cr-Mo creep strength-enhanced ferritic (CSEF) steels are mainly used in nuclear and thermal power plants. In the present investigation, a systematic study on fracture surface morphologies of tensile and impact tested specimens and mechanical properties of cast and forged (C&F) P92 steel was performed for various heat treatment conditions. The heat treatment was carried out in normalizing temperature range of 950-1150 degrees C and then tempered to a fixed tempering temperature of 760 degrees C. The effect of varying normalizing temperatures before and after tempering on microstructure evolution, tensile properties, Vicker's hardness and Charpy toughness was studied. The normalizing temperature before and after tempering was having a noticeable effect on mechanical properties of as-received P92 steel. The fracture surface of impact and tensile tested samples was also studied for various normalizing temperatures with or without tempering. Fracture surface morphology was affected by the presence of secondary phase carbide particles. The fraction area of cleavage facets on the tensile fracture surface was found to be increased with an increase in the normalizing temperature. The fractured tensile specimens were characterized by transgranular ductile dimples, tear ridges and transgranular cleavage facets for various heat treatments. The fracture mode of impact tested samples was more complex. It showed both quasi-cleavage facets and ductile dimple tearing for various normalizing temperatures.