JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 430, 期 -, 页码 29-35出版社
ELSEVIER
DOI: 10.1016/j.jmmm.2016.11.062
关键词
Barium hexaferrite; Sol-gel technique; VSM; Magnetic properties; Optical properties
资金
- Fatih University Project Office [P50031504_B (10790)]
Ba1-xZnxFe12O19 (0.0 <= x <= 0.3) hexaferrites were produced via sol-gel auto combustion technique. XRD patterns show that all the samples are single-phase M-type barium hexaferrite (BaM). Scanning electron microscopy (SEM) revealed that grains have a size range of 0.5-2 mu m. The magnetic hysteresis (sigma-H) loops revealed the ferromagnetic nature of NPs. The average crystallite sizes were calculated by applying Scherrer equation on the base of XRD powder patterns of all samples and found to be in the range of 16.78-48.34 nm. In particular, Ba1-xZnxFe12O19 (0.0 <= x <= 0.3) hexaferrites have suitable magnetic characteristics (saturation magnetization in a range of 63.00-67.70 emu/g and coercive field in a range of 822-1275 Oe) for magnetic recording and permanent magnets. Effective crystalline anisotropy constants (K-eff) are between 4.20x10(5) and 4.84x10(5) Erg/g. Magnetic moment increased by the substitution of non-magnetic Zn2+ ions. The anisotropy field (H-a) or intrinsic coercivity values above 13255 Oe reveals that all samples are magnetically hard materials. Tauc plots were drawn to specify the direct optical energy band gap (E-g) of NPs. The E-g values are in a narrow range between 1.69 eV and 1.76 eV.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据