期刊
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 423, 期 -, 页码 226-231出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jmmm.2016.09.097
关键词
Y-type hexaferrites; La-Zn substitution; Magnetic properties; Microstructure
The La-Zn substituted nanocrystalline Sr2-xLaxNi2Fe12-xZnxO22 (with x=0.0, 0.4, 0.5, 0.6, 0.7, 0.8 and 0.9) hexaferrites were prepared using sol-gel auto-combustion method to investigate the microstructure and magnetic properties. Fourier transform infrared spectroscopy (FT-IR) spectra showed two main absorption bands at 429 and 594 cm(-1) corresponding to the stretching and vibration of tetrahedral and octahedral groups in S blocks. The X-ray diffraction pattern confirmed the phase formation of Y-type hexaferrite with R-3 m space group which also provided the lattice constants and crystallite sizes of each product. Furthermore, the crystallite size (D) was found to be in the range of 31.4-43.1 nm. Field emission electron microscopy (FESEM) images confirmed that the grain size was reduced from 600 to 150 nm due to the increase of dopant cations and, subsequently, caused soft magnetic properties to improve. By performing a thorough investigation on the M-H hysteresis loops, it was found that the magnetization first increased up to x= 0.7 and then decreased, while coercivity monotonously decreased from 1313 to 569 Oe. This behavior can be attributed to the migration of Fe3+ ions from spin-down to spin-up, local strains, deviation of spin arrangement and strength of superexchange interactions.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据