期刊
ACS APPLIED ENERGY MATERIALS
卷 2, 期 10, 页码 7527-7534出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsaem.9b01513
关键词
proton exchange membranes; fuel cells; partially fluorinated ionomers; pendant sulfonic acid groups; sulfonated polymers
资金
- New Energy and Industrial Technology Development Organization (NEDO)
- Ministry of Education, Culture, Sports, Science and Technology (MEXT) Japan [KAKENHI JP18K04746, JP18H02030, JP18H05515, JP18K19111]
The six kinds of sulfonated poly(arylene perfluoroalkylene) (SPAF) ionomers with pendant multi-sulfophenylene groups were designed and synthesized to apply to fuel cells as proton exchange membranes. The SPAF polymers possessed high ion exchange capacity (IEC) values (2.07-2.15 mequiv g(-1)), good solubility in organic solvents, and high molecular weight, providing the flexible membranes by solution casting. Compared with our previous SPAF-MM membrane (with no pendant sulfophenylene groups), the introduction of the pendant sulfophenylene groups resulted in the significant improvement of proton conductivity, whereas it did not deteriorate the other favorable membrane properties, such as gas impermeability and mechanical properties. The SPAF-BM, as the chosen membrane, exhibited higher fuel cell performance than that of our previous SPAF-MM membrane under low humidified conditions. During the open circuit voltage (OCV) hold test, the SPAF-BM cell showed the low average decay of 40 mu Vh(-1) and kept high OCV even after 1000 h. Post-test analyses proved that the SPAF-BM membrane after the OCV hold test retained the original fuel cell performance without practical changes in the molecular structure and molecular weight due to the high chemical stability of SPAF-BM.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据