The Characteristics of Mineral Trioxide Aggregate/Polycaprolactone 3-dimensional Scaffold with Osteogenesis Properties for Tissue Regeneration

Introduction: The aim of this study was to investigate whether the mineral trioxide aggregate/polycaprolactone (MTA/PCL) hybrid 3-dimensional (3D) scaffold supplies a suitable microenvironment for the osteogenic differentiation of human dental pulp cells (hDPCs) and to further consider the effect of the MTA/PCL composite on the biological performance of hybrid scaffolds. Methods: MTA was suspended in absolute alcohol and dropped slowly into PCL that was generated with the printable MTA-matrix. Then, the MTA/PCL composite was prepared into highly uniform scaffolds with controlled macropore sizes and structure using a 3D printing technique. Mechanical properties and the apatite precipitation of the scaffolds were evaluated as well as the cell response to the scaffolds by culturing hDPCs. Results: The results showed that the MTA/PCL 3D scaffold had uniform, 450-m, high-porosity (70%) macropores and a compressive strength of 4.5 MPa. In addition, the MTA/PCL scaffold could effectively promote the adhesion, proliferation, and differentiation of hDPCs. Conclusions: The 3D-printed MTA/PCL scaffolds not only exhibited excellent physical and chemical properties but also enhanced osteogenesis differentiation. All of the results support the premise that this MTA/PCL porous scaffold would be a useful biomaterial for application in bone tissue engineering.