期刊
NEW JOURNAL OF CHEMISTRY
卷 44, 期 3, 页码 780-790出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c9nj04414k
关键词
-
资金
- Natural Science Foundation of Tianjin China [19JCZDJC37800]
- Science and Technology Plans of Tianjin China [18PTSYJC00180]
- National Natural Science Foundation of China [21878230]
Carbon nanotubes (CNTs) and graphene oxide (GO) were sprayed on flexible polyethylene terephthalate (PET) substrates to prepare CNT and GO-CNT transparent conductive films (TCFs). For the GO-CNT TCFs, when the mass ratio of GO to CNTs was 0.2, a relatively low sheet resistance of 90.4 omega sq(-1) at a transmittance of 87% (550 nm) was obtained with an average sigma(dc)/sigma(opt) value of 28.9. Poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) solution without or with ethylene glycol (EG) added was sprayed on the surface of the GO-CNT films to obtain P/GO-CNT and P(E)/GO-CNT films, respectively. P(E)/GO-CNT films were post-treated with sulfuric acid to obtain P(E,S)/GO-CNT TCFs. The addition of PEDOT:PSS can permeate into the pores of networks and densify the GO-CNT networks, increasing the conductivity and wettability and decreasing the roughness of the films. Additional EG can reduce the Coulomb force between PEDOT and PSS and change the morphology of PEDOT, and at the same time sulfuric acid treatment can effectively remove PSS from the PEDOT:PSS layer. The P(E,S)/GO-CNT 0.2 TCFs exhibited a sheet resistance of 46.3 omega sq(-1) at a transmittance of 87.5% (550 nm) with an average sigma(dc)/sigma(opt) value of 56.1. The organic light emitting diodes were successfully fabricated, and the mechanism of how the electrical conductivity of the hybrid film increased was also investigated.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据