Cleaner extraction of vanadium; Three-phase reaction; Vanadium slag; Spontaneously formed porous pellet; Mechanisms
资金
- National Natural Science Foundation of China [51374023]
The traditional industrial practice for extracting vanadium from vanadium slag involves a Na2CO3-Na2SO4-NaCl-added pellet roasting at 800 degrees C followed by a water leaching. Some chlorine and hydrogen chloride are emitted by this process. About 80% of vanadium and 5% of chromium can be extracted in this case. The disposal of this leaching residue containing high contents of chromium and vanadium is still an unsolved environmental problem so far. A complete extraction of vanadium and chromium from vanadium slag might be an ultimate solution. In order to efficiently extract vanadium from vanadium slag, an innovative NaOH-added pellet was applied in this work to replace traditional Na2CO3-Na2SO4-NaCladded pellet. It was found that the volume of NaOH-added pellet increased by 144% and many cavities were formed spontaneously throughout the pellet during the roasting at 700 degrees C. A solid phase (dry slag minerals), a liquid phase (molten liquid drops of NaOH with low viscosity) and a gas phase (O-2) were involved in a three-phase reaction occurred inside the pellet. The spontaneously formed cavities created good kinetic conditions for the three-phase reaction. The V extraction was thus increased from traditional 80% at 800 degrees C to current 99% at 700 degrees C. The V extractionwas increased by 39% when a NaOH-added pellet sample was used instead of a NaOH-added powder sample. The roles of porous pellet and liquid NaOH drops were explored. The V extraction dramatically increased with increasing temperature in the temperature range of 400 degrees C to 600 degrees C and reached a maximum at 700 degrees C. The V extraction dramatically increased with time within the first 15 min at 700 degrees C. The optimal roasting temperature, time and R(Na/ Cr) value for the V extraction were 700 degrees C, 15 min and 7.67, respectively. The V extraction was 99.2% under the optimal conditions. The cooling rate of the roasted pellet had no significant effect on V extraction. The vanadium from the vanadium slag was mainly contained in a vanadium-containing spinel phase (Mn, Fe)(V, Cr, Ti) 2O4. The oxidation of V3+ probably went through the following process: (Mn, Fe)(V, Cr, Ti)(2)O-4 ->(Cr0.15V0.85)(2)O-3 -> NaVO2 -> Na3VO4. This process avoided the emission of toxic gas. (C) 2017 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据