期刊
JOURNAL OF CLEANER PRODUCTION
卷 161, 期 -, 页码 357-361出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jclepro.2017.05.121
关键词
Wool waste; Keratin; Decoloration; Electrospinning; Nano-membranes
资金
- Open Foundation of Zhejiang Province Key Laboratory on the Formation of yarn materials and Compound processing technology [MTC2014-002]
- Jiaxing Project of Science and Technology [2014AY21006]
Wool keratin and wool keratin/poly(ethylene oxide) nanofibrous membranes were prepared through the decoloration of dyes in the wool waste and extraction and electrospinning of regenerated wool keratin. The effect of pH, ironphthalocyanine and H2O2 concentration on catalytic oxidation were also studied. Under the support of ironphthalocyanine with better structure stability compared with other metal-lophthalocyanines, most azo groups of dyes could be broken into colorless products under the catalytic oxidation of ironphthalocyanine and H2O2 at pH = 10, and the decolorization percentage was about 94.2% in 210 min. To improve the spinnability of the extracted wool keratin, poly(ethylene oxide) was introduced into the keratin electrospinning and with the increased loading ratio of poly(ethylene oxide), the diameter of the nanofibers thickened with a value of 546 312 nm for the 70/30 wool keratin-poly(ethyleneoxide) nanofibrous membranes. Decolorizing dyes and extracting wool keratin for the preparation of keratin-based nanomembranes was benefit to recycles of wool waste and decreases the environmental pressure. (C) 2017 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据