Environmentally clean ceramics from printed circuit board sludge, red mud of bauxite treatment and steel slag

The main purpose of this study was the development of new ceramic composites from three industrial wastes: printed circuit board, red mud from bauxite processing and steel slag, completely replacing clay and sand as traditional natural raw materials. Rectangular test specimens with 20 x 60 mm in size were compacted with 3 MPa pressure, dried and sintered at temperatures of 1000 degrees, 1050 degrees, 1100 degrees, 1150 degrees, 1200 degrees, 1250 degrees and 1275 degrees C for 3 h. The resulting ceramic flexural strength was 15.39 MPa; water absorption ranged between 4.47 and 38.45%; linear shrinkage, between 1.17 and 16.90% and bulk density, from 2.10 to 2.56 g/cm(3). The leaching and solubility tests show a reliable bonding of all metals until a level far above the requirements of Brazilian sanitary standards. (C) 2017 Elsevier Ltd. All rights reserved.