期刊
JOURNAL OF APPLIED PHYSICS
卷 121, 期 22, 页码 -出版社
AMER INST PHYSICS
DOI: 10.1063/1.4985065
关键词
-
资金
- Ministry of Trade, Industry & Energy (MOTIE) through the Encouragement Program for The Industries of Economic Cooperation Region [R0004019]
In this work, CdSe quantum dots (QDs) with tunable sizes have been fabricated via photoinduced chemical etching at room temperature, and the related reaction mechanism was investigated. The surface of QDs was oxidized by the holes generated through photon irradiation of oxygen species, and the obtained oxide layer was dissolved in an aqueous solution of 3-amino-1-propanol (APOL) with an APOL: H2O volume ratio of 5:1. The generated electrons promoted QD surface interactions with amino groups, which ultimately passivated surface defects. The absorption and photoluminescence emission peaks of the produced QDs were clearly blue-shifted about 26 nm with increasing time, and the resulting quantum yield for an 8 h etched sample was increased from 20% to 26%, as compared to the initial sample. (C) 2017 Author(s).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据