JOURNAL OF ALLOYS AND COMPOUNDS
卷 725, 期 -, 页码 461-471出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2017.07.163
关键词
Lithium orthosilicate; Solution combustion synthesis; CO2 absorption; Thermal shrinkage
资金
- Board of Research on Fusion Science and Technology (BRFST)
- Institute for Plasma Research (IPR), Bhat, Gandhinagar, India
Phase pure Lithium orthosilicate (Li4SiO4) nanopowder was synthesized by solution combustion method using glycine as the fuel and silicic acid as a silica source. The effect of the fuel- to- oxidizer ratio (Phi(c)) (0.6 e1.0) in the combustion process and phase evolution was studied. We found that by controlling the fuelto- oxidizer ratio of the starting solution phase purity can be achieved at 700 degrees C. Li4SiO4 powder was also prepared by solid state method and phase purity was achieved at 800 degrees C. The surface area, powder morphology, sintering behavior and CO2 capture properties of the Li4SiO4 were investigated. The powder synthesized by solution combustion route showed higher surface area, sinterability and CO2 absorption capacity compared to the solid state route powder. It could be attributed to the nanostructured morphology of the particles. The grain size in the sintered sample could be kept well below 5 mm. The current report provides a novel method to fabricate lithium orthosilicate, and shows promise for application as high temperature CO2 absorption as well as solid breeder in fusion reactor. (C) 2017 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据