Aluminum-magnesium5 (AlMg5); Graphene oxide (GO); Hot-pressing; Tensile strength; Flexural strength; Powder metallurgy
资金
- Research Grant of Pukyong National University
- KACST
- Estonian Ministry of Education and Science projects [TK117, IUT2-24]
Graphene oxide (GO) powder was dispersed in an AlMg5 matrix using high energy ball milling. The obtained blend was then completely densified by hot pressing. No further hardening processing step was performed. Nevertheless, only 1 vol% of GO in the Aluminum alloy matrix leads to a significant improvement of the mechanical resistance. The ultimate tensile strength (540 MPa) and the macro hardness (166 HV) are increased by a factor of 2 compared to the same AlMg5 alloy without nano-particulate material and compacted under the same conditions. The bending strength is even increased by a factor of 4 reaching a value over 800 MPa. The GO powder can be applied as a mechanical reinforcement to other scenarios such as polymer and ceramic systems. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据