JOURNAL OF ALLOYS AND COMPOUNDS
卷 720, 期 -, 页码 408-416出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2017.05.271
关键词
ZnMn2O4; Mn3O4; Electrosynthesis; Nanorods; Supercapacitor
ZnMn2O4/Mn3O4 composite nanostructures were prepared by cathodic electrodeposition followed by heat treatment. A mixed hydroxide precursor was galvanostatically electrodeposited from aqueous solution containing Mn and Zn (as nitrates) and the obtained precursor was annealed to prepare the composite. This composite exhibited much better electrochemical behaviors than bare Mn3O4. Rietveld analysis of the X-ray diffraction (XRD) data showed that the product was composed of Mn3O4, ZnMn2O4 and minor amounts of lambda-MnO2. Furthermore, the obtained composite was characterized by Fourier transform infrared spectrometry (FT-IR) and energy dispersive spectrometry (EDS). Field emission scanning electron micrographs (FE-SEM) and transmission electron micrographs (TEM) revealed coexistence of nanoparticles and high aspect ratio nanorods. Electrochemical performance and ion transport of ZnMn2O4/Mn3O4 composite were studied via galvanostatic charge-discharge (GCD) cycling and electrochemical impedance spectroscopy (EIS). Cyclic voltammetric (CV) measurements showed a maximum specific capacitance of 321.34 F/g at the scan rate of 1 mV/s. 93% of this specific capacitance was retained after 2000 cycles. (C) 2017 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据