JOURNAL OF ALLOYS AND COMPOUNDS
卷 724, 期 -, 页码 666-673出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2017.07.059
关键词
Double perovskite; Structural analysis; Microstructure; Impedance; Solid oxide fuel cell
资金
- Universiti Brunei Darussalam
- Geology Department, Faculty of Science, Universiti Brunei Darussalam
A new series of double perovskite oxides Sr2Fe1-xTixNbO6-delta (x = 0, 0.05 & 0.1) were prepared by traditional solid state reaction method and characterized by X-ray diffraction, scanning electron microscope (SEM), energy dispersive x-ray (EDX), ac impedance and dc four point using Van Der Pauw method. The samples were sintered at 1200 degrees C for 12 h in air to get single phase. Rietveld refinement shows that all composition crystallizes in tetragonal symmetry in the space group I4/m. The lattice parameter were related to the ideal single perovskite a(p) as a approximate to b approximate to root 2a(p), and c approximate to 2a(p). Scanning electron microscope shows increase in porosity with increase of Ti content. Sr2Fe1-xTixNbO6-delta/YSZ shows a good interface with no lamination problem between the two materials. EDX shows that the element contents of the materials synthesized in this study close to the nominal stoichiometry. Chemical compatibility studies with YSZ electrolyte shows no reaction with the anode. A symmetrical cell with the configuration of Sr2Fe1-xTixNbO6-delta vertical bar YSZ vertical bar Sr2Fe1-xTixNbO6-delta (x = 0.05 & 0.1) shows the lowest polarization resistance of 49.80 Omega cm(2) and the highest ac conductivity of 3.57 x 10(-3) S cm(-1) in dry H-2/Ar for x = 0.1. The activation energy was found to be 1.20 eV which is almost similar to Sr2FeNbO6-delta as reported in literature. The dc conductivity measurement was highest for SFTN0.1 at 750 degrees C in dry 5% H-2/Ar with a value of 1.17 S cm(-1). (C) 2017 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据