JOURNAL OF ALLOYS AND COMPOUNDS
卷 714, 期 -, 页码 126-132出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2017.04.194
关键词
Ordered macro-/mesoporous structure; Sulfur/carbon composite cathode; Lithium/sulfur battery; Dual-templating method
资金
- National Natural Science Foundation of China [21606068, 21406052]
- Scientific Innovation Grant for Excellent Young Scientists of Hebei University of Technology [2015001]
- program for the Outstanding Young Talents of Hebei Province [BJ2014010]
- Science Research Foundation for Selected Overseas Chinese Scholars, Ministry of Human Resources and Social Security of China [CG2015003002]
Herein, we report a three- dimensionally (3D) ordered macro-/mesoporous carbon (3DOM-mC) as a sulfur supporter for rechargeable lithium/sulfur (Li/S) batteries. The 3DOM-mC is prepared by a dual-templating method via using silica crystal as hard template, triblock copolymer EO20PO70EO20 as soft template and resol (phenol/formaldehyde) as the carbon source. The as-synthesized 3DOM-mC possesses a large BET surface area of 818.5 m(2) g(-1), ordered interconnected macropores and ordered mesopores on the macropore walls. The 3DOM-mC is then composited with sulfur to obtain the sulfur/3DOM-mC (S/3DOM-mC) hybrids by a simple solvothermal synthesis process. In Li/S batteries, the S/3DOM-mC composite shows a high initial discharge capacity of 1042 mAh g(-1), with 703 mAh g(-1) remaining after 100 cycles at 0.2 C. Furthermore, at a high rate of 2.5 C, it can still deliver a high capacity of 357 mAh g(-1), with a capacity recuperability of 85% as the current back to 0.5 C. The great electrochemical performance is attributed to its unique hierarchical structure with 3D ordered interconnected macropores that can provide the rapid mass transport and ordered mesopores that can trap polysulfides via physisorption. (C) 2017 Elsevier B.V. All rights reserved.