W-30 wt.% Cu composite powders with homogenous distribution of W and Cu nanoparticles were successfully synthesized by a sol-gel procedure combined with hydrogen reduction. These ultrafine particles smaller than 150 nm exhibited favorable sinterability when densified by field assisted sintering technique (FAST) at the temperatures below the melting point of Cu. Moreover, the as-sintered composites inherited the ultrafine and homogeneous characteristics of the initial particles. The final densities of the sintered samples showed a strong dependence on the sintering temperature and applied pressure. By increasing the sintering temperature or pressure, denser composites with higher thermal conductivity and lower coefficient of thermal expansion (CTE) could be obtained. Specifically, the samples sintered at 950 degrees C under 120 MPa for 10 min achieved a maximum relative density of 97.3%, exhibiting an excellent thermal conductivity (235.48 W/(m K)) and a relatively low CTE of 9.27 x 10(-6)/ K. (C) 2017 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据