SiC micropowder; Electroless etching process; UV irradiation; Photoluminescence
Spin coated thin films of pure Poly Vinyl Alcohol (PVA) and PVA mixed with porous SiC microparticles were prepared in order to be used in an optical device. An electroless method was used for producing porous silicon carbide powder under UV irradiation was investigated. The electroless process was chosen because it does not require electrical contact during etching like in anodic one. Silver nanolayer coated SiC particles was formed by polyol process prior the etching and served both as an anode, catalyst and mask for the reduction of a chemical oxidant. The etchant was composed of HF and different oxidants in water. Various porous morphologies are presented and studied as a function of etchant concentration, oxidant type, etching time, and wavelength of irradiation. Morphological, optical and photoluminescence characterizations of SiC micropowder embedded in PVA matrix and deposited as thin films on glass substrates are reported. We concluded that the chemical etching conditions of SiC powder seems to have a large impact on the resulting properties. We noticed that thin film based on SiC powder etched under UV light of 254 nm using K2S2O8 as oxidant, at reaction temperature of 80 degrees C for t = 40min exhibited the best photoluminescence property. (C) 2017 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据