An ultrathin (6.2 nm) ferroelectric La0.1Bi0.9FeO3 (LBFO) film was epitaxially grown on a 0.7 wt% Nb-doped SrTiO3 (001) single-crystal substrate by carrying out pulsed laser deposition to form a Pt/La0.1Bi0.9FeO3/Nb-doped SrTiO3 heterostructure. The LBFO film exhibited strong ferroelectricity and a low coercive field. By optimizing the thickness of the LBFO film, a resistance OFF/ON ratio of the Pt/LBFO (similar to 6.2 nm)/NSTO heterostructure of as large as 2.8 x 10(5) was achieved. The heterostructure displayed multi-level storage and excellent retention characteristics, and showed stable bipolar resistance switching behavior, which can be well applied to ferroelectric memristors. The resistance switching behavior was shown to be due to the modulating effect of the ferroelectric polarization reversal on the width of the depletion region and the height of the potential barrier of the LaBiFeO3/Nb-doped SrTiO3 interface.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据