JOURNAL OF MATERIALS CHEMISTRY A
卷 8, 期 18, 页码 9313-9321出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/d0ta01297a
关键词
-
资金
- National Natural Science Foundation of China [51772147, 51502137, U1601214, 51425301]
- National Materials Genome Project [2016YFB0700600]
- Jiangsu Distinguished Professorship Program (2016)
- Postgraduate Research AMP
- Practice Innovation Program of Jiangsu Province [KYCX18_1128, SJCX19_0218]
- Research Foundation of State Key Lab [ZK201906, ZK201805]
Zinc ion batteries have attracted increasing research attention because of their unique merits (low cost, high safety, etc.). However, poor cycle stability, low energy density and sluggish reaction kinetics are still the major challenges for their further development. Exploring electrode materials with high capacity, durability and fast Zn2+ ion diffusion is crucial to address the aforementioned challenges. Herein, we demonstrate that layered VSe2 with a large interlayer spacing could exhibit excellent Zn storage behavior. Even with a micro-sized morphology, it exhibits a high specific reversible capacity of 250.6 and 132.6 mA h g(-1) at 200 and 5000 mA g(-1) and good cycle life. The excellent rate performance is comparable to or even higher than those of other nanosized Zn host materials reported in the literature. The good electrical conductivity, large interlayer spacing and pseudocapacitive storage are responsible for its good performance. Combined electrochemical investigation with X-ray diffraction, X-ray photoelectron spectroscopy, X-ray absorption spectroscopy and scanning electron microscopy techniques reveals that VSe2 undergoes an intercalation/de-intercalation process with good structural stability during cycling, accompanied by the redox of the vanadium element.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据