Structure and defect manipulation are regarded as efficacious strategies to boost the electrochemical activity of electrode materials. Herein, the construction of one-dimensional (1D) porous S-doped Co3O4 nanorods with rich oxygen vacancies is demonstrated through a facile metal-organic framework-engaged strategy. Starting from a Co-NTA (NTA = nitrilotriacetic acid) precursor, the S-doped Co3O4 nanorods were obtained after calcination and sulfurization. As a faradaic electrode material, the S-doped Co(3)O(4)nanorods exhibited enhanced specific capacitance (319.3 C g(-1)at 0.5 A g(-1)) in comparison with the Co(3)O(4)intermediate product (98.3 C g(-1)) and the Co-NTA precursor (40.2 C g(-1)). Besides, it showed an ultra-high rate capability of 83.3% with a 20-fold increase in current density (10 A g(-1)). The hybrid supercapacitor comprising the S-doped Co3O4(cathode) and the activated carbon (anode) showed a high energy density of 38.1 W h kg(-1)at a power density of 800 W kg(-1), and 31.1 W h kg(-1)was maintained at 8000 W kg(-1). It also has excellent electrochemical stability, and 87.57% of its initial capacitance was maintained after 5000 cycles, demonstrating great prospects in electrochemical energy storage applications. The excellent energy storage property of the S-doped Co3O4 is due to its unique 1D S-doped Co3O4 porous nanorod structure,i.e., large surface area, easy diffusion of ions, good conductivity, and rich redox reactions. This work may pave the way for the fabrication of desirable electrode materials through vacancy defects and nano-/microstructure engineering.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据