INTERNATIONAL JOURNAL OF FATIGUE
卷 140, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijfatigue.2020.105820
关键词
Early fatigue damage process; Damage interaction; In-situ monitoring; Digital Image Correlation
资金
- China Scholarship Council [201706290028]
This study investigates the early fatigue damage of cross-ply carbon/epoxy laminates. The aim is to unfold the damage accumulation process, understand the interaction between different damage mechanisms, and quantify their contribution to stiffness degradation. Tension-tension fatigue tests were performed, while edge observation and DIC technique monitored the damage evolution. It was found that different accumulation process and interactive levels between transverse matrix cracks and delamination exist for specimens with similar stiffness degradation. A linear increase of stiffness degradation was observed with the increase of matrix crack density, while the growing trend of stiffness degradation converged with the increase of delamination.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据