JOURNAL OF LUMINESCENCE
卷 227, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.jlumin.2020.117565
关键词
Ca3Al2O6; Phosphor; XRD; Gel combustion; Thermoluminescence; Trap parameters
类别
Undoped Ca3Al2O6 phosphor was successfully synthesized through a gel-combustion method using different fuels. It was characterized by X-ray diffraction (XRD) technique and its cubic phase structure was confirmed from XRD pattern. TL data were recorded from room temperature (RT) to 500 degrees C in the heating rate of 2 degrees C/s. The glow curves of Ca3Al2O6 sample exposed to different beta doses (0-200 Gy) exhibited a significant glow peak at about 184 degrees C. The TL intensity of the glow peak exhibited very good linearity between 0.1 and 10 Gy. Following this, it was decreased at higher doses which was referred to this effect as monotonic dose dependence. Initial rise (IR), peak shape (PS), and variable heating rate (VHR) methods were used to estimate trapping parameters. Computerized glow curve deconvolution (CGCD) method via TLAnal software was also applied to estimate the number of peaks and kinetic parameters corresponding to the main glow curve in Ca3Al2O6 sample. The trapping activation energy of the main dosimetric peak was calculated to be around 1.30 eV for all methods. Present findings confirm that Ca3Al2O6 host is a promising candidate for applications in environmental dosimetry as one depicts good TL dose response with adequate sensitivity and linearity.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据