POLYMER
卷 209, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymer.2020.122954
关键词
Thienothiophene; Triphenylamine; Electropolymerization; Cyclic voltammetry; Electrochromic; EIS; Capacitance
资金
- Higher Education Council of Turkey (YOK)
- TUBITAK [100/2000 YOK, TUBITAK BIDEP 2211A]
- Istanbul Technical University [42325]
- Unsped Global Lojistik
N-(4-(4-thieno [3,2-b]thiophen-3-yl-phenyl)phenye-N-phenylbenzenamine (TTpTPA), synthesized by Suzuki cross-coupling reaction, was electropolymerized in DCM/CAN (4/1 v/v) mixture, containing 0.1 M Bu4NPF6. Charge storage property of the polymer, investigated by electrochemical impedance spectroscopy measurements at different potentials, suggested that the highest capacitance value could be obtained at its anodic peak potentials. Double layer and low-frequency capacitances were found to be C-DL = 369 Fg(-1) and C LF = 447 Fg(-1) at E-DC = 1.23 V. These values are in good agreement with the results obtained from equivalent circuit model. Electrochromic properties of the corresponding polymer, PolyTTpTPA, were investigated by spectroelectrochemical measurements, which indicated that while the polymer had a gold-orange color in its neutral state with an absorption maximum of 378 nm, it became blue in its oxidized state with an absorption maximum of 850 nm. Chronocoulometric measurement of the film exhibited a residence time of 10 s, indicating a fast response time and stable photoelectrochemical behavior, which are the most important parameters for electrochromic applications. In addition, hydrophobic property of the film, having a contact angle measurement of 115 degrees, is a good advantage for electronic applications for outdoor and wet areas. This work demonstrates that reversible capacitive current property and porous structure of PolyTTpTPA, supported by SEM and AFM images, make it a good candidate for electrochromic and capacitor devices.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据