Cathodoluminescence(CL) analysis of ZnSe crystal from 350 nm to 850nm at room temperature

期刊

JOURNAL OF INFRARED AND MILLIMETER WAVES
卷 39, 期 5, 页码 601-604

出版社

SCIENCE PRESS
DOI: 10.11972/j.issn.1001-9014.2020.05.010

关键词

ZnSe crystal; Cathodoluminescence (CL); Zn inclusion

类别

资金

  1. National Key RD Project [2016YFB0500600]

向作者/读者索取更多资源

As-received ZnSe crystal has been examined by cathodoluminescence spectroscopy ranging from 350nm to 850nm at room temperature for internal defects and inclusions. Two cathodoluminescence peaks of 462nm and 453nm were detected, of which the former was identified as intrinsic cathodoluminescence of ZnSe and the latter was caused by the crystal defect. The Zn: Se ratio of 6:4 was found by energy dispersive x-ray spectroscopy (EDS), and the extrinsic cathodoluminescence peak of 453nm was attributed to additional Zn in excess of ZnSe stoichiometry.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.2
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据