期刊
RSC ADVANCES
卷 10, 期 73, 页码 44824-44833出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/d0ra08316j
关键词
-
资金
- Science and Engineering Research Board (SERB), DST India [EMR/2016/00l977]
- Technology Mission Division Energy and Water, DST India [DST/TMD/MES/2K18/194(G)]
- CSIR-CSMCRI
This work describes the suitability of a polyethylene styrene-DVB based interpolymer cation exchange membrane for use in a highly alkaline redox flow battery (RFB) with a [Fe(TEA)OH](2-)/[Fe(TEA)OH](-) and Fe(CN)(6)(3-)/Fe(CN)(6)(4-) redox couple. The alkaline stability of the membrane for 1440 h was evaluated in 5 N NaOH containing a 200 mM Fe(CN)(6)(3-)/Fe(CN)(6)(4-) redox couple. It was assessed according to the changes in the electrochemical and physicochemical properties. The performance of the membrane was evaluated over 40 charge-discharge cycles at a current density of 5 mA cm(-2) current in a designed RFB cell. The obtained average coulombic efficiency (CE) was 92%, energy efficiency (EE) was 75%, voltage efficiency (VE) was 82% and volumetric efficiency was 34%. Under identical experimental conditions, the values of CE, EE, and VE for Nafion (R)-112 were 99%, 75%, and 76%, respectively. These results indicate the suitability of the polyethylene styrene-DVB based interpolymer cation exchange membrane for use in an alkaline RFB.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据