Fused deposition modeling; Stress (materials); Composite materials; PLA; ABS; Flexural properties
This paper analyzed the mechanical properties of ABS parts manufactured through fused filament fabrication compared with PLA and PLA-wood specimens. The study found that layer height and nozzle diameter are the most significant factors affecting the mechanical resistance in pieces generated through additive manufacturing.
Purpose The aim of this paper is to analyze the mechanical properties of acrylonitrile-butadiene-styrene (ABS) parts manufactured through fused filament fabrication and compare these results to analogous ones obtained on polylactic acid (PLA) and PLA-wood specimens to contribute for a wider understanding of the different materials used for additive manufacturing. Design/methodology/approach With that aim, an experimental based on an L27 Taguchi array was used to combine the specific parameters taken into account in the study, namely, layer height, nozzle diameter, infill density, orientation and printing velocity. All samples were subjected to a four-point bending test performed according to the ASTM D6272 standard. Findings Young's modulus, elastic limit, maximum stress and maximum deformation of every sample were computed and subjected to an analysis of variance. Results prove that layer height and nozzle diameter are the most significant factors that affect the mechanical resistance in pieces generated through additive manufacturing and subjected to bending loads, regardless of the material. Practical implications The best results were obtained by combining a layer height of 0.1 mm and a nozzle diameter of 0.6 mm. The comparison of materials evidenced that PLA and its composite version reinforced with wood particles present more rigidity than ABS, whereas the latter can experience further deflection before break. Originality/value This study is of interest for manufacturers that want to decide which is the best material to be applied for their application, as it derives in a practical technical recommendation of the best parameters that should be selected to treat the material during the fused filament fabrication process.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据