期刊
MATERIALS TODAY-PROCEEDINGS
卷 38, 期 -, 页码 743-748出版社
ELSEVIER
DOI: 10.1016/j.matpr.2020.04.192
关键词
Nickel-based composite; Graphene; Spark plasma sintering; Microstructure; Properties
资金
- R & I Directorate, Tshwane University of Technology, Department of Mechanical Engineering, Mechatronics and Industrial Design
In this study, Graphene/Inconel 738LC composites were synthesized using spark plasma sintering technique, and the microstructural features were investigated. It was found that with the increase in sintering temperature, the hardness property of the composites increased significantly, while porosity and fracture toughness decreased. The composite sintered at 1100 degrees C showed the highest hardness value and the lowest porosity.
Graphene/Inconel 738LC composites were synthesized using spark plasma sintering technique and the microstructural features were investigated using Optical microscope, Scanning electron microscope and X-ray diffraction machine. The microhardness, porosity and fracture toughness of the graphene-reinforced Inconel 738LC matrix composites were obtained. The processing parameters used were sintering pressure of 40 MPa, heating rate of 100 degrees C/min, soaking time of 5 min and varied sintering temperatures between 1000 and 1100 degrees C. The results show that spark plasma sintering is a viable powder metallurgy technique to develop graphene-reinforced Inconel 738LC composite. The increase in sintering temperature shows that there was significant increase in the hardness property of the sintered composites while the porosity and fracture toughness significantly reduced. Intermetallic and solid solution phases were formed within the microstructure which enhanced the strength of the sintered composites. In this study, the highest microhardness value (469 Hv), lowest porosity (1.47%) and fracture toughness value (26) was obtained in the composite sintered at 1100 degrees C. (C) 2019 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据