CHEMICAL LEACHING OF Al3Ni AND Al3Ti ALLOYS AT ROOM TEMPERATURE

Al3Ni and Al3Ti alloys were prepared by arc melting and exposed to chemical leaching in 5M NaOH at room temperature. In case of Al3Ni alloy, Al reached phases react with the leaching solution to produce nanoporous nickel with a pore diameter in the range of similar to 10-20 nm. Only pure Al phase of Al3Ti alloy chemically reacts with the production of a dense wrinkled surface with a wrinkle size of similar to 50-100 nm.

Automated summary

Al3Ni alloy forms nanoporous nickel with pore diameter of 10-20 nm after chemical leaching, while Al3Ti alloy produces a dense wrinkled surface with wrinkle size of 50-100 nm through chemical reaction with only the pure Al phase.