Effects of low and high temperature plasma nitriding on electrochemical corrosion of steel

期刊

MATERIALS TODAY-PROCEEDINGS
卷 39, 期 -, 页码 1367-1371

出版社

ELSEVIER
DOI: 10.1016/j.matpr.2020.04.692

关键词

Corrosion; Polarization; Plasma nitriding; Tool steel; XRD

向作者/读者索取更多资源

This study investigates the plasma nitriding of tool steel at different temperatures and its impact on corrosion resistance. Results show that nitriding at higher temperatures enhances corrosion resistance more effectively.
This study concerns plasma nitriding of tool steel at different temperatures and its effects on corrosion resistance. Inside the nitriding reactor steel samples were placed on the sample holder after metallographic polishing and then the vacuum chamber was evacuated to a pressure of similar to 0.5 Pa. At a lower temperature of 450 degrees C and the higher temperature of 550 degrees C nitriding was performed for a fixed duration of 10 h. All the nitrided and the bare steel samples studied under X-ray diffraction (XRD) and scanning electron microscopic analysis/energy dispersive X-ray spectroscopy (EDS). Iron nitride (FexN, x = 2-3, 4) peaks were revealed in the nitrided steels after XRD analyses. EDS revealed the increased amount of nitrogen in the nitrided sample treated at 550 degrees C. For the assessment of corrosion resistance of these steel samples potentiodynamic polarization tests were performed in 3.5% NaCl. On comparison, it was found that the steel nitrided at higher temperature is more effective in enhancing the corrosion resistance. (C) 2020 Elsevier Ltd. All rights reserved.Y

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

3.8
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据