The research demonstrates that directional etching of chromium using fluorine-oxygen-based plasma is feasible, providing high etch rates while maintaining reasonable directionality. The fluorine-oxygen-based plasma can achieve high etch rates for chromium oxide, and using a sequential fluorine-oxygen-based plasma etching process can improve selectivity while preserving directionality.
Chromium is a frequently encountered material in modern nanofabrication, directly as a functional material (e.g., photomask generation) or indirectly as a hard mask (e.g., to etch quartz). With the continuous downscaling of devices, the control of the feature size of patterned Cr and CrOx becomes increasingly important. Cr and CrOx etching is typically performed using chlorine-oxygen-based plasma chemistries, but the nanoscale imposes limitations. In this work, directional etching is demonstrated for the first time using fluorine-oxygen-based plasma. Two cases are studied to demonstrate the Cr etch performance: (i) a plasma mixture of SF6+O-2 and (ii) a switching SF6/O-2 procedure in which the plasmas are used sequentially. The proposed mixture performs with Cr etch rates (ERs) up to 400nm/min at 300W platen power and is highest when the SF6/O-2 gas ratio is similar to 0.75%, i.e., almost pure O-2 plasma. The profile shows reasonable directionality but the etch selectivity is low, less than 5 toward Si, due to the high generated self-bias of 420V. The selectivity of the plasma mixture can be improved at a lower plasma power, but this is accompanied with considerable undercut. The etching of CrOx proceeds without the need for O-2 in the feed, and, therefore, the ER can reach much higher values (beyond 2000nm/min at 300W). As the plasma mixture seems to be inadequate, a sequential process is studied with improved selectivity while preserving directionality. The high selectivity is achieved by using relatively low plasma power (to ensure a low self-bias) and the directionality is due to the time separation of the SF6 and O-2 plasmas and a controlled directional removal of CrFx etch inhibiting species. Using such a switched procedure at 30W plasma power, a selectivity beyond 20 with good profile directionality is achieved and having an etch rate of similar to 1nm per cycle (or 7nm/min).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据