Preparation of Agave tequilana Weber Nanocrystalline Cellulose and its Use as Reinforcement for Acrylic Hydrogels

Nanocrystalline cellulose (NCC) was prepared from Agave tequilana Weber blue variety via acid hydrolysis. The NCC was used in forming acrylic acid/acrylamide hydrogels (AA/AM), (80/20 w/w), crosslinked with N-N-methylene bisacrylamide (MBA) at addition levels of 1, 2, 4, and 8 wt% of the monomeric phase. The NCC was dosed at 0.1, 0.5, and 1.0 wt%. Two synthesis routes were used. In the first route, polymerization was performed immediately after mixing the components. In the second route, the mixture of the components was kept at 2 degrees C +/- 1 degrees C for 24 h before the polymerization (thermal treatment). All the hydrogels were characterized by nuclear magnetic resonance (NMR), water absorption tests, scanning electron microscope (SEM) analysis, and rheology tests. The NCC particles had a diameter of approximately 75 nm. The hydrogels that were subjected to the thermal treatment reached the equilibrium after approximately 72 h. The un-treated hydrogels reached the equilibrium after approximately 58 h. The thermally treated samples had a lower swelling degree and the swelling degree decreased as the crosslinking degree and the NCC concentration increased. The swelling kinetics followed the Schott's pseudo-second-order.

Automated summary

Nanocrystalline cellulose was prepared from Agave tequilana Weber blue variety via acid hydrolysis and used to form hydrogels. The properties of hydrogels under different treatment methods were studied.