CONSTRUCTION AND BUILDING MATERIALS
卷 96, 期 -, 页码 673-678出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2015.08.089
关键词
Fly ash; Geopolymer; Alkali-activated; High strength
In this laboratory work, high compressive and flexural tensile strength of alkali activated fly ash geopolymer mortars were presented. Class F fly ash was used throughout the study. NaOH was used as alkali medium that provides high pH value. Also, the factors influencing the compressive and flexural tensile strength were investigated. A total of 216 fly ash geopolymer mortar samples were prepared. Heat curing temperature, heat curing duration and alkali (Na) concentration were chosen as the influencing parameters of strengths. Mortar mixture parameters were 3 and 1/3 for sand-binder ratio, and water-binder ratio, respectively. Na concentrations of the mortar mixtures were changed from 4% to 20% with 2% increment step. Heat curing temperatures were changed from 45 to 115 degrees C with 10 degrees C increment step. Heat curing durations were chosen as 24, 48 and 72 h. For each combination of influencing parameter, three prismatic specimens with 40 mm x 40 mm x 160 mm dimensions were prepared using a three-cell mortar cast. After heat curing period in a laboratory oven, the samples were left to cool down to room temperature, then compressive and flexural strengths were measured as described in its respective standard. Very high compressive and flexural tensile strength obtained, which were as high as 120 and 15 MPa respectively. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据