LaCoO3 powders were prepared by the urea combustion method and used as electrode materials for supercapacitors. The degradation mechanism of LaCoO3-based symmetric supercapacitors was discussed, showing that the degradation is mainly caused by irreversible redox reactions during the charge and discharge process. The results indicate that the performance degradation becomes more intense with the increase in potential window and current density.
In this paper, LaCoO3 powders were prepared by the urea combustion method and used as electrode materials for supercapacitors. The effect of the potential window and the current density on the performance degradation of LaCoO3 electrodes during the cycling test was analyzed. The degradation mechanism of LaCoO3-based symmetric supercapacitors was discussed. The results of the cycling test show that: with the increase in potential window and current density, the performance degradation in the cycling test becomes more intense. The results of cyclic voltammetry tests, galvanostatic charge-discharge tests, X-ray photoelectron spectroscopy tests and KOH electrolyte concentration measurements before and after the cycling test show that the degradation of the supercapacitors is mainly caused by the occurrence and accumulation of irreversible redox reactions during the charge and discharge process, which reduces the ratio of Co2+/Co3+ and the number of oxygen vacancies.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据