期刊
EUROPEAN JOURNAL OF WOOD AND WOOD PRODUCTS
卷 76, 期 2, 页码 549-562出版社
SPRINGER
DOI: 10.1007/s00107-017-1233-4
关键词
-
资金
- COST Action [FP1303, STSM-FP1303-010615-060045]
- Slovak Research and Development Agency [APVV-14-0506, APVV-15-0235]
In this study, the physical and mechanical properties of plywood panels made from pre-compressed birch (Betula verrucosa Ehrh.) veneer were evaluated. Veneer sheets underwent short-term thermo-mechanical (STTM) compression at temperatures of 150 or 180 A degrees C and at pressures of 0.5, 1.0, 1.5, 2.0, 2.5, 3.0 or 3.5 MPa for a period of 1 min prior to adhesive being applied and pressed into panels using phenol formaldehyde adhesive at 100 g/m(2) spread rate; this was one-third less than the adhesive spread used for the control panels (150 g/m(2)). The pressing pressure was 1.0 MPa, which was almost half of the pressure used for the control panels (1.8 MPa); and pressing time was 3 min, also half of the pressing time used for the control panels (6 min). The results showed that surface roughness of compressed veneer, water absorption and thickness swelling of plywood panels made from compressed veneer were significantly improved. The shear strength values of plywood panels made from compressed birch veneer even with reduced adhesive spread were higher than those of plywood panels made from uncompressed veneer. The findings in this study indicated that compression of birch veneer could be considered as an alternative to produce more eco-friendly (owing to smaller adhesive spread) value-added material with enhanced properties.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据