Effects of Selected Printing Parameters on the Fire Properties of 3D-Printed Neat Polylactic Acid (PLA) and Wood/PLA Composites

The effects of selected printing parameters on the fire properties of additively produced composites from neat polylactic acid (PLA) and wood/PLA filaments were investigated. The reaction to fire of the 3D-printed specimens was tested according to the ISO 5660-1 cone calorimeter test method. The results showed that the properties of the specimens when exposed to fire were significantly affected by the incorporation of wood flour into the PLA filament. It was also interesting that PLA specimens had much better reactions to fire than the wood/PLA specimens. Time to ignition was found to be much longer in the 3D-printed PLA specimens. Although the maximal heat release rate was a little higher in the PLA than the wood/PLA specimens, the duration of HRR was longer for the wood/PLA specimens. The initial mass of the specimens was smaller in the wood/PLA composites, but during the radiant heat exposure the mass typically decreased slower than in the PLA specimens.

Automated summary

The study investigated the effects of selected printing parameters on the fire properties of additively produced composites from PLA and wood/PLA filaments. Results showed that the incorporation of wood flour into PLA significantly affected the properties of specimens exposed to fire, with PLA specimens exhibiting better reactions to fire and longer time to ignition compared to wood/PLA specimens. Additionally, while the maximal heat release rate was slightly higher in the PLA specimens, the duration of HRR was longer for wood/PLA specimens.