Study on the Influence of Three Factors on Mass Loss and Surface Fractal Dimension of Concrete in Sulfuric Acid Environments

When exposed to sulfuric acid environments, the service life of concrete structures would be reduced due to the high alkalinity of concrete. The influence of three factors including water/cement ratio, the pH value of the solution, and the chemical composition of the aggregate on the resistance of concrete subjected to sulfuric acid has been widely investigated by previous researchers. This paper aims to investigate the influence of these three factors on the durability evaluation indicators including mass loss and surface fractal dimension through orthogonal experiments, which has been reported rarely in previous research. Four combinations of coarse and fine aggregate including gravel and river sand, gravel and crushed marble sand, crushed marble stone and river sand, and crushed marble stone and marble sand were adopted, and three water/cement ratios including 0.35, 0.45, and 0.55 were selected, and the sulfuric acid solution pH values 0.95, 2, and 4 were chosen in this paper. The results showed that the larger the water/cement ratio, the smaller the mass loss and the surface fractal dimension of the specimens, and with the decrease of the pH value of the sulfuric acid solution, the mass loss and the surface fractal dimension of the specimens would be increased. The concrete specimen containing gravel and river sand had the greatest surface fractal dimension and greatest mass loss, while the concrete specimen containing crushed marble sand had a smaller surface fractal dimension and a smaller mass loss. The dominant and secondary order of three factors on mass loss and surface fractal dimension of concrete subjected to sulfuric acid was the pH value of the solution > the chemical composition of the aggregate > the water/cement ratio.

Automated summary

This study investigated the influence of water/cement ratio, solution pH value, and aggregate chemical composition on the durability of concrete exposed to sulfuric acid through orthogonal experiments. The results showed that a higher water/cement ratio led to smaller mass loss and surface fractal dimension of specimens, while a lower pH value of the sulfuric acid solution resulted in greater mass loss and surface fractal dimension.