Hierarchical porous ZSM-5 (HP-ZSM-5) was constructed using organosilanes as the growth inhibitors for CO2 capture. The properties of adsorbents were characterized by X-ray diffraction, N-2 adsorption/desorption, scanning electron microscopy, temperature-programmed desorption of carbon dioxide, and Al-27 magic angle spinning nuclear magnetic resonance. It was found that HP-ZSM-5 samples synthesized by organosilanes had a significant effect on the microstructure and morphology. CO, adsorption capacity of HP-ZSM-5 was up to 58.26 cm(3) g(-1) at 0 degrees C and 1 bar, significantly higher than that of the ZSM-5 sample. The effective improvement of CO2 adsorption performance mainly originated from the micro-/mesoporous composite structure and complex surface morphology, which can provide low -resistant pathways for CO2 through the porous network. Besides, in situ Fourier transform infrared spectroscopy was carried out to study the adsorption process on adsorbents, and the results indicated that a faster physical adsorption process was achieved as a result of the introduction of mesopores.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据