insulating presspaper; nanofibrillated cellulose; tensile strength; breakdown behavior
资金
- National Basic Research Program of China (973 Program) [2014CB239501]
- Science and Technology Project of China Southern Power Grid [KY2014-2-0016]
This study explores the possibility of enhancing both mechanical and breakdown properties of insulating presspaper by the introduction of an organic nano additive. Four different concentrations of nanofibrillated cellulose (NFC) were taken into account: 0.5 wt %, 2.5 wt %, 5 wt %, and 10 wt %. Presspaper containing no NFC was also prepared as a reference. Obtained samples were characterized by scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FTIR), and X-ray diffraction (XRD). Mechanical properties and breakdown behaviors were measured. Results show that the addition of 10 wt % NFC to softwood fibers can achieve the best performance. Tensile strength of reference presspaper is 109 MPa, whereas that of presspaper modified by 10 wt % NFC is 136 MPa, resulting in a 25% increase. The improved tensile strength can be attributed to the increased density and inter fiber bond strength. More importantly, presspaper reinforced by 10 wt % NFC can also achieve enhanced AC and DC breakdown strengths, which are 19% and 21% higher than those of the reference presspaper. It is concluded that NFC is likely to be a promising nano additive for cellulose insulation.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据