Preparation of efficient piezoelectric PVDF-HFP/Ni composite films by high electric field poling

Poly(vinylidene fluoride) (PVDF) and its copolymers have been widely studied due to their excellent piezoelectricity and ferroelectricity. In this study, composite films are prepared by adding Ni nanoparticles (0.00-0.3 wt%) into poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) matrix by solution casting, uniaxial stretching, and high electric field poling. It is found that when the maximum electric field E (max) for poling is 130 MV m(-1), the calibrated open circuit voltage of the pure PVDF-HFP films reaches 3.12 V, which is much higher than those poled by a lower electric field (70 MV m(-1): 1.40 V; 90 MV m(-1): 2.29 V). This result shows that the effect of poling on the generated output voltage is decisive. By adding 0.1 wt% Ni nanoparticles, it increases to 3.84 V, 23% higher than that of the pure PVDF-HFP films. To further understand the enhancement mechanism, the effects of Ni nanoparticles on initial crystallization, uniaxial stretching, and high electric field poling are investigated by X-ray diffraction, scanning electron microscope, Fourier transform infrared spectroscopy, and differential scanning calorimetry.

Automated summary

In this study, composite films were prepared by adding Ni nanoparticles into poly(vinylidene fluoride-co-hexafluoropropylene) matrix. It was found that the maximum electric field for poling had a decisive effect on the generated output voltage. By adding Ni nanoparticles, the output voltage increased by 23%.