Barium sodium niobate (BNN) ceramics with different amounts of BaO-Na2O-Nb2O5-P2O5 (BNNP) glass were prepared and the effect of glass content on the structural, microstructural, and dielectric properties of the ceramics was investigated. The results showed that adding BNNP glass improved the microstructure and significantly increased the dielectric constant of the ceramics.
Barium sodium niobate Ba2NaNb5O15 (BNN) ceramics with different amounts of BaO-Na2O-Nb2O5-P2O5 (BNNP) glass were prepared via the conventional solid-state method. The effect of glass content on structural, microstructure and dielectric properties of BNN ceramics was investigated. The XRD results showed that no secondary phase was formed after adding BNNP glass. It was found that such additions reduce the average grains size and refine the microstructure of the obtained ceramics. Moreover, the samples exhibited a stable dielectric constant over the temperature range of 25 degrees C-150 degrees C and their dielectric constants were significantly improved. The ceramic with 7.5 wt% BNNP glass content showed a dielectric constant which is more than twice as much as that of pure BNN ceramic, as well as a low dielectric loss less than 5%. (C) 2021 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据